Study of composite AlO-Ce:YMgAlSiO ceramic phosphors.
Clicks: 315
ID: 56490
2019
The nominal composition of AlO-Ce:YMgAlSiO (A-Ce:YMASG) ceramic phosphors was fabricated by the vacuum sintering technique. The introduction of AlO as a second phase partially enters the crystal lattice, which was confirmed by the composition changing of the samples through x-ray diffraction measurement. An impurity phase of YMgSiO was observed in Ce:YMASG and disappeared with the introduction of AlO at the concentration of 10 wt. %. When the content of AlO increased to 30 and 50 wt. %, the second phase of AlO was measured with actual weight ratios of 7.72 and 20.55 wt. %, respectively. The third phase of MgAlO was found with the further addition of AlOat 70 wt. %; the weight ratios of Ce:YMASG, AlO, and MgAlO were 68.756, 18.457, and 12.787 wt. %, respectively. The luminescent characters of the samples were measured by the photoluminescence spectra and electroluminescent spectra. With the increase of AlO from 0 to 30 wt. %, the emission wavelength of Ce plummeted from 610 to 552 nm, and the luminous efficacy of the samples increased from 35 to 65 lm/W.
| Reference Key |
tian2019studyoptics
Use this key to autocite in the manuscript while using
SciMatic Manuscript Manager or Thesis Manager
|
|---|---|
| Authors | Tian, Yanna;Tang, Yanru;Yi, Xuezhuan;Chen, Jie;Ao, Gang;Hao, Deming;Lin, Yandan;Zhou, Shengming; |
| Journal | optics letters |
| Year | 2019 |
| DOI | 10.1364/OL.44.004845 |
| URL | |
| Keywords |
Citations
No citations found. To add a citation, contact the admin at info@scimatic.org
Comments
No comments yet. Be the first to comment on this article.